NanoFoil


NanoFoil is the name trademarked by the Indium Corporation for a reactive multi-layer foil material, sometimes referred to as a pyrotechnic initiator of two mutually reactive metals, aluminium and nickel, sputtered to form thin layers to create a laminated foil.[1] On initiation by a heat pulse, delivered by a bridge wire, a laser pulse, an electric spark, a flame, or by other means, the aluminium and nickel undergo self-sustaining exothermic reaction, producing an intermetallic compound nickel aluminide (NiAl). The reaction occurs in solid and liquid phase only, without releasing any gas.

Such multilayer materials, whether nickel-aluminium, aluminium-titanium, or titanium-amorphous silicon, are used for joining materials by reactive bonding.

NanoFoil is a trademark name of Reactive NanoTechnologies. The technology was developed in Lawrence Livermore National Laboratory from the technology used to fabricate multilayer optics for extreme ultraviolet and x-ray ranges.[2]

The foil is made in a range of thicknesses, e.g. 60, 80, 100, and 150 micrometers. The flame front propagation rate ranges generally between 7.5–9 m/s. The reaction temperature can reach up to 1500 °C for a millisecond. The energy released is approximately 1200 to 1300 joules per gram.[3] The velocity and temperature of the reaction can be controlled by adjusting the thickness of the layers. Typical thickness is 50 nm per a bilayer.[2] The thin layers maximize the contact between the metal and lower the activation energy for the reaction, normally too high to allow reaction between bulk aluminium and bulk nickel. The layers are deposited by sequential sputtering of alternately nickel and aluminium.

Nanofoil will ignite on heating to at least 250 °C in rate of at least 200 °C/min. Slower heating will anneal the material, causing loss of its pyrotechnic properties. For electrical initiation, a momentary contact at 10A/5V is sufficient; for ohmic contact, 120-150 amperes is needed for a 15 micrometer diameter contact, and 250-300 A for a 300 micrometer contact.[4] It can be also ignited by a heat paper. When the flame front reaches the edge of the material, particles of molten metal can be ejected, causing voids in the bond; this can be prevented by simultaneous ignition from more sides, so the flame fronts meet in the middle, confined by the substrates.[5]

Nanofoil can be both cut and ignited by a laser. The pulse width and power determines if the material will be cut or initiated.[3]

Nanofoil is frequently used for soldering and brazing, as a heat source. When sandwiched between the components to be joined, either with a foil of solder on each side, using solder precoated components, or using solder-coated NanoFoil, it uniformly delivers significant amount of heat energy across the entire area, melting the solder and only locally heating the surface of the substrates, lowering the heat load on the component in comparison with soldering/brazing in a furnace. An externally applied even pressure during reaction and cooling serves to ensure a good homogeneous joint without voids. This process is known as NanoBond.[4] Significantly dissimilar materials can be bonded without cracking: semiconductors, metals, ceramics, and polymers.[2] The energy is deposited very locally, without significant heating of the bulk of the substrates, which reduces problems with mismatched thermal expansion coefficients between the materials and allows their joining at room temperature.

The NanoBond process can be used in assembly of electronics, die attachment to heatsinks where high temperature stability is required (e.g. high-power LEDs or concentrated photovoltaics solar panels, soldering together layers of composite armor plates, bonding of large sputtering targets made of ceramics or refractory metals where normal indium based solders cannot be used, and other applications where a uniform joint over large area has to be created.[6]

NanoFoil can be used as a pyrotechnic heat source, a replacement of potassium chlorate/iron pellets, for thermal batteries. It reacts faster than the conventional composition, reaches higher temperatures, and heat buffers of inert metal (e.g. steel) are needed to lower the peak temperature and prolong the heat delivery.[7]

NanoFoil can be also used as an electrically initiated pyrotechnic initiator, e.g. to ignite solid propellants, and in decoy flares.

NanoFoil is not significantly sensitive to electrostatic discharge.[5]

NanoFoil-like composites can be employed in weapons as reactive materials, enhancing the energy delivery to the targets by the projectiles or their fragments.

Other similar intermetallic compositions used in pyrotechnics are titanium-boron and aluminium-palladium ("Pyrofuze").

See also

References

  1. ↑ http://www.indium.com/nanofoil/
  2. 1 2 3 https://www.llnl.gov/str/October05/Barbee.html
  3. 1 2 http://blogs.indium.com/blog/nanofoil/0/0/nanofoil-basics-activation-part-i
  4. 1 2 http://www.indium.com/_dynamo/download.php?docid=932
  5. 1 2 http://blogs.indium.com/blog/tommy-acchione/0/0/nanofoilr-basics-activation-part-ii
  6. ↑ http://blogs.indium.com/blog/nanofoil/0/0/nanofoilr-nanotech-comes-to-indium-corporation
  7. ↑ http://armyscienceconference.com/manuscripts/H/HP-08.pdf
This article is issued from Wikipedia - version of the 6/17/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.